Growth and characterization of GaInNAs by molecular beam epitaxy using a nitrogen irradiation method

We propose an innovative technique, making use of the In segregation effect, referred as the N irradiation method, to enhance In-N bonding and extend the emission wavelength of GaInNAs quantum wells (QWs). After the formation of a complete In floating layer, the growth is interrupted and N irradiation is initiated. The majority of N atoms are forced to bond with In atoms and their incorporation is regulated independently by the N exposure time and the As pressure. The effect of the N exposure time and As pressure on the N incorporation and the optical quality of GaInNAs QWs were investigated. Anomalous photoluminescence (PL) wavelength red shifts after rapid thermal annealing (RTA) were observed in the N-irradiated samples, whereas a normal GaInNAs sample revealed a blue shift. This method provides an alternative way to extend the emission wavelength of GaInNAs QWs with decent optical quality. We demonstrate light emission at 1546 nm from an 11-nm-thick QW, using this method and the PL intensity is similar to that of a 7-nm-thick GaInNAs QW grown at a reduced rate. (C) 2008 Elsevier B.V. All rights reserved.

1310 nm GaInNAs triple quantum well laser with 13 GHz modulation bandwidth

The emission wavelength of a GaInNAs quantum well (QW) laser was adjusted to 1310 nm, the zero dispersion wavelength of optical fibre, by an appropriate choice of QW composition and thickness and N concentration in the barriers. A triple QW design was employed to enable the use of a short cavity with a small photon lifetime while having sufficient differential gain for a large modulation bandwidth. High speed, ridge waveguide lasers fabricated from high quality material grown by molecular beam epitaxy exhibited a damped modulation response with a bandwidth of 13 GHz.

Magnetic barrier on strained graphene: A possible valley filter

We put forward a two-terminal valley filter based on a bulk graphene sheet under the modulations of both a local perpendicular magnetic field and a substrate strain. When only one of the two modulations is present, no valley polarization can be generated. A combination of the two modulations leads to a different (but not opposite) shifts of the K and K' valleys, which could be utilized to generate a valley-polarized current. The degree of the valley polarization can be tuned by the strain strength and the inclusion of a scalar potential. The valley polarization changes its polarity as the local magnetic field switches its direction.

Effects of molecular structure on the permeability and permselectivity of aromatic polyimides

Permeability coefficients of H-2, O-2, and N2 were measured under 10 atm at the temperature from ambient temperature up to 150 degrees C in a series of structurally different aromatic homo- and copolyimides, which were prepared from 4,4'-oxydianiline (ODA) or 4,4'-methylene dianiline (MDA) with various aromatic dianhydrides. The study shows that the molecular structure of the polyimides strongly influences gas permeability and permselectivity. As a result, the permeability coefficients of the polyimide membranes for each gas vary by over two orders of magnitude. In general, among the polyimide membranes studied, the increase in permeability of polymers is accompanied by the decrease in permselectivity, and the MDA-based polyimide membranes have higher permeability than ODA-based ones. Among the polyimides prepared from bridged dianhydrides, the permeability coefficients to H-2, O-2, and N-2 are progressively increased in the order BPDA < BTDA < ODPA similar to TDPA < DSDA ( SiDA < 6FDA, while H-2/N-2 and O-2/N-2 permselectivity coefficients are progressively decreased in the same order. The copolyimide membranes, which were prepared from 3,3',4,4' biphenyltetracarboxylic dianhydride (BPDA), bis(3,4-dicarboxyphenyl)dimethylsilane dianhydride (SiDA), and ODA, have favorable gas separation properties and are useful for H-2/N-2 separation applications. (C) 1996 John Wiley & Sons, Inc.

含硅聚酰亚胺和有机硅改性的联苯型聚酰亚胺透气性能的研究

本文合成了一系列均聚和共聚酰亚胺,研究了它们对H_2、O_2和N_2三种气体的透过性能与分子结构之间的关系。结果表明,在30℃和6atm的条件下,SiDA-ODA对H_2和O_2的透过系数分别为11.7和0.764Barrer,比BPDA-ODA高一个数量级;H_2/N_2和O_2/N_2分离系数分别为113和7.4在(BPDA/SiDA)-ODA共聚物中,随着SiDA含量的增加,其透氢系数P_(H_2)和透氧系数P_(O_2)均有较大的增加,而H_2/N_2和O_2/N_2分离系数则降低。当SiDA含量占二酐组分的60%时,P_(H_2)和P_(H_2)/P_(N_2)分离系数分别达8.78Barrer和147。